Annealing of ~12.5 nm thick vacuum-deposited organic thin film of 5 wt% Ir(pp...
This trajectory begins from a vacuum-deposition simulation of 5 wt% Ir(ppy)2(acac):CBP on graphene that has just reached an approximate film thickness of 12.5 nm (replica 1 of... -
Spontaneous penetration of water into a vacuum deposited 6wt% Ir(ppy)2(acac):...
A layer of water was placed over a vacuum deposited 6wt% Ir(ppy)2(acac):CBP organic thinfilm. No water was placed within the film. Water spontaneously diffused into the film... -
Oxygen diffusion in a vacuum deposited 6wt% Ir(ppy)2(acac):CBP organic thinfi...
20 oxygen molecules were inserted at random positions within a vacuum deposited 6wt% Ir(ppy)2(acac):CBP thinfilm and allowed to diffuse (replicate 3 of 3). -
Oxygen diffusion in a vacuum deposited 6wt% Ir(ppy)2(acac):CBP organic thinfi...
20 oxygen molecules were inserted at random positions within a vacuum deposited 6wt% Ir(ppy)2(acac):CBP thinfilm and allowed to diffuse (replicate 2 of 3). -
Oxygen diffusion in a vacuum deposited 6wt% Ir(ppy)2(acac):CBP organic thinfi...
20 oxygen molecules were inserted at random positions within a vacuum deposited 6wt% Ir(ppy)2(acac):CBP thinfilm and allowed to diffuse (replicate 1 of 3). -
Water diffusion in a vacuum deposited 6wt% Ir(ppy)2(acac):CBP organic thinfil...
20 water molecules were inserted at random positions within a vacuum deposited 6wt% Ir(ppy)2(acac):CBP thinfilm and allowed to diffuse (replicate 3 of 3). -
Water diffusion in a vacuum deposited 6wt% Ir(ppy)2(acac):CBP organic thinfil...
20 water molecules were inserted at random positions within a vacuum deposited 6wt% Ir(ppy)2(acac):CBP thinfilm and allowed to diffuse (replicate 2 of 3). -
Water diffusion in a vacuum deposited 6wt% Ir(ppy)2(acac):CBP organic thinfil...
20 water molecules were inserted at random positions within a vacuum deposited 6wt% Ir(ppy)2(acac):CBP thinfilm and allowed to diffuse (replicate 1 of 3).